Investigation on the regeneration and corrosion characteristics of an anodized aluminum plate regenerator.

Document Type

Journal Article

Publication Date

2018

Keywords

falling film regeneration; internal heating; corrosion; surface energy; anodized aluminum plate

DOI

10.3390/en11051209

Abstract

The traditional vapor compression cooling system (VCS) has been criticized for its heavy reliance on electricity consumption and limited control ability of humidity. Compared with the VCS, the liquid desiccant cooling system (LDCS) is more efficient by handling the sensible and latent load separately. The present study investigated the regeneration and corrosion characteristics of an anodized aluminum plate regenerator for the first time. Comparative tests were conducted to present the regeneration and corrosion characteristics of the normal and anodized regenerator. The influence of internal heating on the regeneration performance was also identified. The results showed that the corrosion rate was reduced from 0.0005218 mm/year for normal aluminum to 0.000011 m/year for anodized one under the same operating conditions. However, pitting corrosion was observed at operating conditions with high solution temperature, as the anodized layer of anodized aluminum was damaged due to the high temperature. Compared with the normal aluminum regenerator, the anodized one had an average enhancement of 24% and 23.7% in terms of regeneration rate and effectiveness, respectively. It was attributed to the increment of surface energy from 26.4 mN/m for normal aluminum to 47.6 mN/m for anodized plate. Besides, it was found that, compared with adiabatic one, the internally-heated regenerator improved the regeneration rate by 6.0%~38% and the regeneration effectiveness by 6.3%~32% depending on the operating conditions. The advantage of present study is that it can guide the design of anodized aluminum regenerator for LDCS.

Source Publication

Energies

Volume Number

11

Issue Number

5

ISSN

1996-1073

First Page

1

Last Page

15

This document is currently not available here.

Link to Publisher’s Version